X16CrMo5-1

2023-05-17 16:18:08 來源：鋼鐵之家閱讀量：0

牌號	X16CrMo5-1
歐標鋼號	1.7366
對應標準	EN 10222-2-2017 壓力用途用鋼制鍛件第2部分具有高溫特性的鐵素體和馬氏體鋼 Steel Forgings for Pressure Purposes. Part 2:Ferritic and Martensitic Steels with Specified Elevated Temperature Properties
歸類	合金鋼

X16CrMo5-1 化學元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Mo
最小值	-	-	0.3	-	-	4	0.45
最大值	0.18	0.4	0.8	0.025	0.01	6	0.65

碳當量計算

X16CrMo5-1 機械性能

厚度 t mm	抗拉強度 σ_b Mpa	屈服點 σ_s Mpa	斷后伸長率或延伸率 δ %	沖擊吸收能量 KV2 J
t≤300	410~510	≥205	I：≥18，tr/t：≥16	≥40
t≤300	640~780	≥420	I：≥16，tr/t：≥14	≥27

① I = longitudinal to main forging directions；tr = transverse to main forging directions；t = tangential.
② Maximum room temperature for the impact test is 20 °C. By option, impact testing may be carried out at 0°C, with the condition to fulfil the impact values as stated in this table.
③ Until the yield point criteria are harmonized in the various national codes, determination of ReH may be replaced by determination of Rp0.2. In this case Rp0.2 values are 10 MPa lower for ReH values up to 355 MPa and 15 MPa lower for ReH values greater than 355 MPa.

熱處理制度（僅供參考）

A= annealed; QT= quenched and tempered; NT= normalized and tempered. a = air; f = furnaced; o = oil.

注：本資料來源于互聯網的公開資源整理，我們不保證這些資料的準確性、完整性和適用性。這些資料僅供您參考，不應用于任何商業用途或決策依據。本資料所記載的技術信息是說明產品的代表性特點和性能的參考值，對于因誤用或不當使用本資料所記載的信息等而造成的損害恕難承擔責任，敬請周知。